產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 物理性能 | 密度 | ASTM D792 | 1.53 | |||
| 機(jī)械性能 | 抗壓強(qiáng)度 | 5 mm/min, 3.20 mm, 23 ℃ | ASTM D695 | 202 | MPa | |
| 拉伸強(qiáng)度 | 23℃ | ASTM D638 | 140 | MPa | ||
| 拉伸模量 | 23℃ | ASTM D638 | 10000 | MPa | ||
| 彎曲模量 | 23℃ | ASTM D790 | 8970 | MPa | ||
| 彎曲強(qiáng)度 | 23℃ | ASTM D790 | 200 | MPa | ||
| 斷裂點(diǎn)伸長(zhǎng)率 | 23℃ | ASTM D638 | 2.6 | % | ||
| 低溫缺口沖擊強(qiáng)度 | ASTM D256 | 101 | J/m | |||
| 缺口沖擊強(qiáng)度 | - | -40℃ | ASTM D256 | 101 | J/m | |
| - | 23℃ | ASTM D256 | 112 | J/m | ||
| 非缺口沖擊強(qiáng)度 | - | -40℃ | ASTM D256 | 1120 | J/m | |
| - | 23℃ | ASTM D256 | 998 | J/m | ||
| 熱性能 | 熱變形溫度 | - | 0.45Mpa,未退火 | ASTM D648 | 220 | ℃ |
| - | 1.8Mpa,未退火 | ASTM D648 | 205 | ℃ | ||
| 線性熱膨脹系數(shù) | 平行流動(dòng)方向 | 73 to 130°F (23 to 55℃) | ASTM E831 | 0.000030 | cm/cm/℃ | |
| 垂直流動(dòng)方向 | 73 to 130°F (23 to 55℃) | ASTM E831 | 0.000090 | cm/cm/℃ | ||
| 熔點(diǎn) | 225 | ℃ | ||||
| 阻燃等級(jí) | - | 0.750 mm | UL 94 | HB | ||
| - | 1.50 mm | UL 94 | HB | |||
| - | 3.00 mm | UL 94 | HB | |||
| 其它性能 | 極限氧指數(shù) | ASTM D2863 | 19 | % | ||