| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 比重 | ASTM D792 | 1.41 | g/cm3; | |
| 熔體質(zhì)量流動(dòng)速率 | ASTM D1238 | 27 | g/10 min | ||
| 成型收縮率 | flow,3.00MM | ASTM D955 | 2.0 | % | |
| 吸水率 | Equilibrium,23℃,60%rh | ASTM D570 | 0.22 | % | |
| 洛氏硬度 | M-Scale | ASTM D785 | 80 | ||
| 機(jī)械性能 | 拉伸強(qiáng)度 | Yield,23℃ | ASTM D638 | 62.0 | MPa |
| 拉伸伸長(zhǎng)率 | Break,23℃ | ASTM D638 | 40 | % | |
| 彎曲模量 | 23°C | ASTM D790 | 2650 | MPa | |
| 彎曲強(qiáng)度 | 23°C | ASTM D790 | 91.0 | MPa | |
| 剪切強(qiáng)度 | 2.00mm | ASTM D732 | 55.0 | MPa | |
| Izod缺口沖擊強(qiáng)度 | 3.20mm | ASTM D256 | 59.0 | J/m | |
| 電氣性能 | 表面電阻率 | ASTM D257 | 1.0E+16 | ohms | |
| 體積電阻率 | ASTM D257 | 1.0E+14 | ohm·cm | ||
| 電氣強(qiáng)度 | ASTM D149 | 19 | kV/mm | ||
| 介電常數(shù) | 1E+6 Hz | ASTM D150 | 3.70 | ||
| 介質(zhì)損耗因數(shù) | 1E+6 Hz | ASTM D150 | 0.0070 | ||
| 熱性能 | 熱畸變溫度 | 0.45MPa,未退火 | ASTM D648 | 158 | °C |
| 熱畸變溫度 | ASTM D648 | 110 | °C | ||
| 熔融溫度 | 165 | °C | |||
| 線性熱膨脹系數(shù) | flow,20 to 80°C | ASTM D696 | 0.00013 | cm/cm/°C | |
| 其它性能 | 阻燃等級(jí) | 0.8mm | UL 94 | HB | |