產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 熔體流動速率 | 200℃,5kg | ASTM D-1238 | 0.9 | g/10min |
| 比重 | 23℃ | ASTM D-792 | 1.077 | ||
| 機(jī)械性能 | 引張強(qiáng)度 | 1/8",6mm/min | ASTM D-638 | 786(11150) | kg/cm2(lb/in2) |
| 延伸率 | 1/8",6mm/min | ASTM D-638 | 7 | % | |
| 彎曲強(qiáng)度 | 1/4",2.8mm/min | ASTM D-790 | 1244(17643) | kg/cm2(lb/in2) | |
| 彎曲彈性率 | 1/4",2.8mm/min | ASTM D-790 | 35280(49754) | kg/cm2(lb/in2) | |
| IZOD缺口沖擊強(qiáng)度 | 1/4",23℃ | ASTM D-256 | 2.1(0.39) | kg.cm/cm(fg-lb/in) | |
| IZOD缺口沖擊強(qiáng)度 | 1/8",23℃ | ASTM D-256 | 2.5(0.48) | kg.cm/cm(fg-lb/in) | |
| 硬度 | 1/4" | ASTM D-785 | 85 | M Scale | |
| 熱性能 | 軟化點 | 1/8",50℃/hr | ASTM D-1525 | 103.5(218) | ℃(℉) |
| 熱變形溫度 | 1/4",120℃/hr,退火 | ASTM D-648 | 99.5(211)) | ℃(℉) | |
| 熱變形溫度 | 1/4",120℃/hr,未退火 | ASTM D-648 | 90.5(195) | ℃(℉) | |