產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 熔體指數(shù) | ASTM D1238 | 11 | g/10min | |
| 密度 | ASTM D792 | 1.01 | g/cm3 | ||
| 成型收縮率 | ASTM D955 | 0.0065 | |||
| 吸水率 | ASTM D570 | 0.07 | % | ||
| 機(jī)械性能 | 硬度 | ASTM D2240 | 68 | D | |
| 拉伸模量 | 23℃ | ASTM D638 | 1310 | MPa | |
| 屈服拉伸強(qiáng)度 | 23℃ | ASTM D638 | 26 | MPa | |
| 斷裂伸長(zhǎng)率 | 23℃ | ASTM D638 | 250 | % | |
| 彎曲模量 | 23℃ | ASTM D790 | 1170 | MPa | |
| 彎曲強(qiáng)度 | 23℃ | ASTM D790 | 31 | MPa | |
| Izod沖擊強(qiáng)度 | 23℃ | ASTM D256 | 43 | J/m | |
| 電氣性能 | 體積電阻率 | ASTM D257 | ＞1E13 | ||
| 表面電阻率 | ASTM D257 | ＞1E14 | |||
| 熱性能 | 熱變形溫度 | 1.8Mpa | ASTM D648 | 70 | ℃ |
| 熱變形溫度 | 0.46Mpa | ASTM D648 | 77 | ℃ | |
| 維卡軟化點(diǎn) | ASTM D1525 | 86 | ℃ | ||
| 阻燃性 | UL94 | HB | |||